REFRACTORY PRODUCTS

Al2O3:45-51%;

ZrO2:32-40%;

SiO2:12-15%;

Al₂O₃:≥48%;

ZrO₂:≥30%;

Bulk density:≥3.2g/cm³;

ZrO₂:≥6%;

Al₂O₃:≥48%;

Bulk density:≥2.8g/cm³;

ZrO₂:≥65%;

Bulk densit:y≥3.75g/cm³;

Cold crushing strength:≥80MPa;

Al₂O₃:≥62%;

Cr₂O₃:≥10%;

Cold Crushing Strength:≥100MPa;

Al₂O₃:≥80%;

Bulk Density:≥2.75g/cm³;

Cold Crushing Strength:≥85MPa;

Al₂O₃:≥95%;

Bulk density:≥3.15g/cm³;

Apparent Porosity:≤18%;

Al₂O₃:≥70%;

Cr₂O₃:≥10%;

Bulk Density:≥3.3g/cm³;

Al₂O₃:≥62%;

Cr₂O₃:≥10%;

Bulk density:≥3.25g/cm³;

Al₂O₃:90-99%;

Bulk Density:2.8-3.2g/cm³;

Size:Ф6-Ф70;

Al₂O₃:≥75%;

SiC+SiO₂:≥30%;

Bulk Density:≥2.65g/cm³;

Also Called:Silica Mullite Brick;

Al₂O₃:60-65%;

Bulk Density:≥2.55g/cm³;

SiO₂:≥97%;

Bulk Density:≥1.86g/cm³;

Cold Crushing Strength:≥40MPa;

Al₂O₃:≥45%;

Apparent Porosity:≤15%;

Cold Crushing Strength:≥50MPa;

Al₂O₃:75-77%;

Bulk Density:2.650g/cm³;

Cold Crushing Strength:≥60MPa;

Al₂O₃:55-82%;

Bulk Density:2.25-2.7g/cm³;

Refractoriness(SK):36-40;

Al₂O₃:≥57%;

Fe₂O₃:≤1.2%;

Bulk Density:≥2.40g/cm³;

Low-Porosity:≤15%;

Low-Iron:≤0.8%;

Low-Creep:≤0.5%;

Al₂O₃:≥65%;

Bulk Densit:≥2.50g/cm³;

Cold Crushing Strength:≥75MPa;

Al₂O₃:≥ 57%;

Bulk density:≥2.40g/cm³;

Cold Crushing Strength:≥60MPa;

Al₂O₃:≥57%;

Fe₂O₃:≤1.2%;

Bulk Density:≥2.40g/cm³;

SiO₂:91%;

Bulk Density:0.8-1.2g/cm³;

Thermal Conductivity :0.26-0.35;

Al₂O₃:90-99%;

Bulk Density:1.35-1.70g/cm³;

Cold Crushing Strength:8-20MPa;

Al₂O₃:40-70%;

Bulk Density:0.60-1.10g/cm³;

Thermal Conductivity:0.20-0.60;

Al₂O₃:≥48%;

Bulk Density:0.6-1.2g/cm³;

Thermal Conductivity :0.25-0.50;

Bulk Density:0.6-1.3g/cm³;

Thermal Conductivity:0.25-0.55;

Cold Crushing Strength:1.5-8MPa;

Al₂O₃:46-95%;

Refractoriness:1300-1790℃;

Application:Brick Masonry;

Type:CA50,CA70,CA80;

Al₂O₃:50-82%;

Initial Setting Time:30-240min;

Al₂O₃:46%-60%;

Fe₂O₃: 0.7%-1.0%;

Operating Temp:1300-1500℃;

ZrO₂:≥30%;

Al₂O₃:≥50%;

Bulk Density:≥2.85g/cm³;

ZrO₂:≥63%;

Bulk Density:≥3.3g/cm³;

Max Particle Size:5mm;

Al₂O₃:≥45%;

Bulk Density:1.-1.8g/cm³;

Operating Temp:1300-1500℃;

SiC:76-85%;

Bulk Density:≥2.24g/cm³;

Feature:Wear resistant;

Bulk Density:0.8-1.3g/cm³;

Operating Temp:1200-1300℃;

Cold Crushing Strength:2.0-20MPa;

Al₂O₃:42-85%;

Refractoriness:≥1640℃;

Bulk Density:2.15-.65g/cm³;

MgO:70-80%;

Al₂O₃:8-20%;

Bulk Density:2.85-3.15g/cm³;

MgO:85-88%;

Bulk Density:2.95g/cm³;

Cold Crushing Strength:≥80MPa;

MgO:87-97.5%;

Bulk Density:2.85-3.20g/cm³;

Cold Crushing Strength:≥50MPa;

MgO:≥40%;

Cr₂O₃:≥8%;

Cold Crushing Strength:≥25MPa;

MgO:69-85%;

C:5-18%;

Bulk Density:2.85-3.2g/cm3;